Silicon Nitride Ceramic:
Liquid phase sintering is to add A1203 and Y 203 to the silicon carbide powder. After molding, it is sintered at 1800 °C to 2000 y. In the sintering process, A1z team and Y203 form eutectic compound YAG (aluminum garnet Y3Ali [ )) melting point 1760 ° C), the appearance of liquid phase promotes the sintering of Sic and Boron Nitride Ceramic reduces the sintering temperature. Abrasive water jet drilling ceramic technology research compared with cutting processing, drilling processing does not need to consider the influence of nozzle feed rate, processing There are two main problems in the process of relatively simple drilling processing: one is the control of the roughness of the hole wall and the size of the hole; the other is that due to the Zirconia Ceramic Rings divergence of the abrasive water jet, the hole formed by the machining will have a certain degree of inclination. Wan Qingfeng Through experiments, it can be concluded that the larger jet pressure, smaller nozzle traverse speed and proper abrasive flow can effectively increase the drilling depth and improve the quality of the hole wall. However, due to the jet divergence, the hole wall presents a certain taper and points. For the smooth drilling area and the deformation wear area, when the hole being machined is a blind hole, the bottom Machinable Ceramic part will be blocked by the [water pad", and the bag-like structure will be formed. The mathematical method is used to establish the prediction model of drilling depth and surface roughness of the hole wall. The research status and progress of the abrasive water jet processing ceramics respectively. The abrasive holes can be used to ream the existing holes. However, there is no relevant research literature in China. Subsequent research can be applied to the research of reaming processing technology to further broaden the application of abrasive water jet drilling.
properties :
High hardness, high strength, wear resistance, corrosion resistance, high temperature(1200 ° ), good thermal diffusivity, good thermal shock resistance(avoid the temperature changing rapidly), good insulativity, low density. The comprehensive properties are best in most of structure ceramic.
डेटा शीट ↓
Color: Black Grey
Density: ＞3.2g/cm3
Hardness: HRA90
Vickers Hardness (Hv50): ＞1550 HV0.5
Modulus of Elasticity: 290Gpa
Flexural Strength: ＞600Mpa
Compressive Strength: 2500Mpa
Modulus of Elasticity(25°C): 65Gpa
Fracture toughness:＞6.0 Mpam1/2
Maximum Use Temperature: 1200°C
Thermal Conductivity:15-20 W(mK)
Thermal Expansion Coefficient: ＞3.1 10-6/°C
Thermal Shock Resistance: 500 △T°C
Special Heat Capacity: 700 KJ/kg.K
Dielectric Strength: 1 KV/mm
Dielectric Constant: er
Volume Resistivity(20°C): 1.0*10(12)Ω.cm
आवेदन उद्योग :
Machinery, electronic, semiconductor, chemical, petroleum, smelt.
विशिष्ट अनुप्रयोग:
Welding shaft, electronic substrate, plunger, nozzle, slide guide, diesel parts, metal molding, shaft wheels etc.
हमें क्यों चुनें? 1.12 साल के पेशेवर उत्पादन औद्योगिक सिरेमिक कारखाने 2. उच्च गुणवत्ता वाले उत्पाद कम कीमत वाले 3. सबसे कम सहिष्णुता के साथ उच्च परिशुद्धता भाग 4. उत्पादन के लिए समय का समय 5. अनुभवी, पेशेवर और कुशल आर एंड डी टीम का एक समूह 6. चीन और विदेशों में एक अच्छी प्रतिष्ठा। 7.MOQ सीमित नहीं है, छोटी मात्रा का स्वागत है।
8. विगोरस टीम और अच्छी बिक्री के बाद सेवा
Products Show
सामान्य प्रश्न
प्रश्न: क्या आप ट्रेडिंग कंपनी या निर्माता हैं?
A: हम कारखाने हैं।
प्रश्न: आपकी डिलीवरी का समय कब तक है?
A: आम तौर पर यह 5-10 दिन होता है यदि माल स्टॉक में होता है। या यह 15-30 दिन है यदि माल स्टॉक में नहीं है, तो यह मात्रा के अनुसार है।
प्रश्न: क्या आप नमूने प्रदान करते हैं? क्या यह मुफ़्त है या अतिरिक्त है?
A: हाँ, हम मुफ्त शुल्क के लिए नमूना पेश कर सकते हैं लेकिन माल ढुलाई की लागत का भुगतान नहीं करते हैं।
प्रश्न: आपके भुगतान की शर्तें क्या है?
A: भुगतान <= 1000USD, 100% अग्रिम में। भुगतान> = 1000USD, 50% t/t अग्रिम में, शिप से पहले संतुलन।